Preparation and characterisation of hydroxide stabilised ZnO(0001)–Zn–OH surfaces

Abstract

Two different approaches under ambient conditions were developed for the preparation of clean, non-reconstructed, single crystalline ZnO(0001)–Zn surfaces. The surface preparation by a wet chemical etching procedure was compared with the same treatment in combination with a subsequent heat treatment in humidified oxygen atmosphere. Depending on the preparation technique, atomically flat terraces with a width of 100 nm to several micrometers were observed using an atomic force microscope (AFM). The obtained surface structures were further characterized by means of angle resolved X-ray photoelectron spectroscopy (AR-XPS), time-of-flight secondary ion mass spectroscopy (ToF-SIMS), Auger electron spectroscopy (AES) and low energy electron diffraction (LEED) measurements. Based on these results it is shown that the obtained surfaces are, in contrast to surfaces prepared under UHV conditions, stabilised by the adsorption of a monolayer of hydroxides. The important role of H2O during the heat treatment is pointed out by comparing the results of the same heat treatment in the absence of water. H2O turned out to play an important role in the reorganization process of the surface at elevated temperatures, thereby yielding extremely large atomically flat terraces. The terminating edges of these terraces were found to include 120° and 60° angles, thus perfectly reflecting the hexagonal surface structure.

Graphical abstract: Preparation and characterisation of hydroxide stabilised ZnO(0001)–Zn–OH surfaces

Article information

Article type
Paper
Submitted
04 Dec 2006
Accepted
12 Feb 2007
First published
19 Mar 2007

Phys. Chem. Chem. Phys., 2007,9, 2406-2412

Preparation and characterisation of hydroxide stabilised ZnO(0001)–Zn–OH surfaces

M. Valtiner, S. Borodin and G. Grundmeier, Phys. Chem. Chem. Phys., 2007, 9, 2406 DOI: 10.1039/B617600C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements