# Copyright The Royal Society of Chemistry, 1999 # CCDC Number: 182/1236 data_global _publ_requested_journal 'J. Chem. Soc., Chem. Commun.' _publ_section_title ; Crystal structure of the microporous titanosilicate ETS-10 refined from single crystal X-ray diffraction data ; loop_ _publ_author_name _publ_author_address 'Xiqu Wang' ; Department of Chemistry, University of Houston Houston, TX 77204-5641, USA ; 'Allan J. Jacobson' ; Department of Chemistry, University of Houston Houston, TX 77204-5641, USA ; data_ETS-10 _audit_creation_method SHELXL _chemical_name_systematic ; ? ; _chemical_name_common ? _chemical_formula_moiety ? _chemical_formula_structural ? _chemical_formula_analytical ? _chemical_formula_sum 'Na2 O13 Si5 Ti' _chemical_formula_weight 442.33 _chemical_melting_point ? _chemical_compound_source 'synthetic' loop_ _atom_type_symbol _atom_type_description _atom_type_scat_dispersion_real _atom_type_scat_dispersion_imag _atom_type_scat_source 'O' 'O' 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'Na' 'Na' 0.0362 0.0249 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'Si' 'Si' 0.0817 0.0704 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'Ti' 'Ti' 0.2776 0.4457 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' _symmetry_cell_setting ? _symmetry_space_group_name_H-M I4(1)/amd loop_ _symmetry_equiv_pos_as_xyz 'x, y, z' '-x+1/2, -y, z+1/2' '-y+1/4, x+3/4, z+1/4' 'y+1/4, -x+1/4, z+3/4' '-x+1/2, y, -z+1/2' 'x, -y, -z' 'y+1/4, x+3/4, -z+1/4' '-y+1/4, -x+1/4, -z+3/4' 'x+1/2, y+1/2, z+1/2' '-x+1, -y+1/2, z+1' '-y+3/4, x+5/4, z+3/4' 'y+3/4, -x+3/4, z+5/4' '-x+1, y+1/2, -z+1' 'x+1/2, -y+1/2, -z+1/2' 'y+3/4, x+5/4, -z+3/4' '-y+3/4, -x+3/4, -z+5/4' '-x, -y, -z' 'x-1/2, y, -z-1/2' 'y-1/4, -x-3/4, -z-1/4' '-y-1/4, x-1/4, -z-3/4' 'x-1/2, -y, z-1/2' '-x, y, z' '-y-1/4, -x-3/4, z-1/4' 'y-1/4, x-1/4, z-3/4' '-x+1/2, -y+1/2, -z+1/2' 'x, y+1/2, -z' 'y+1/4, -x-1/4, -z+1/4' '-y+1/4, x+1/4, -z-1/4' 'x, -y+1/2, z' '-x+1/2, y+1/2, z+1/2' '-y+1/4, -x-1/4, z+1/4' 'y+1/4, x+1/4, z-1/4' _cell_length_a 7.4866(10) _cell_length_b 7.4866(10) _cell_length_c 27.407(5) _cell_angle_alpha 90.00 _cell_angle_beta 90.00 _cell_angle_gamma 90.00 _cell_volume 1536.2(4) _cell_formula_units_Z 10 _cell_measurement_temperature 293(2) _cell_measurement_reflns_used ? _cell_measurement_theta_min ? _cell_measurement_theta_max ? _exptl_crystal_description ? _exptl_crystal_colour colorless _exptl_crystal_size_max 0.045 _exptl_crystal_size_mid 0.045 _exptl_crystal_size_min 0.010 _exptl_crystal_density_meas ? _exptl_crystal_density_diffrn 1.913 _exptl_crystal_density_method ? _exptl_crystal_F_000 872 _exptl_absorpt_coefficient_mu 1.058 _exptl_absorpt_correction_type SADABS _exptl_absorpt_correction_T_min ? _exptl_absorpt_correction_T_max ? _exptl_special_details ; ? ; _diffrn_ambient_temperature 293(2) _diffrn_radiation_wavelength 0.71073 _diffrn_radiation_type MoK\a _diffrn_radiation_source 'fine-focus sealed tube' _diffrn_radiation_monochromator graphite _diffrn_measurement_device 'Siemens SMART/CCD diffractometer' _diffrn_measurement_method ? _diffrn_standards_number ? _diffrn_standards_interval_count ? _diffrn_standards_interval_time ? _diffrn_standards_decay_% ? _diffrn_reflns_number 4035 _diffrn_reflns_av_R_equivalents 0.1757 _diffrn_reflns_av_sigmaI/netI 0.0880 _diffrn_reflns_limit_h_min -9 _diffrn_reflns_limit_h_max 9 _diffrn_reflns_limit_k_min -8 _diffrn_reflns_limit_k_max 9 _diffrn_reflns_limit_l_min -35 _diffrn_reflns_limit_l_max 34 _diffrn_reflns_theta_min 2.82 _diffrn_reflns_theta_max 28.38 _reflns_number_total 532 _reflns_number_observed 426 _reflns_observed_criterion >2sigma(I) _computing_data_collection 'SMART' _computing_cell_refinement 'SAINT' _computing_data_reduction 'SAINT' _computing_structure_solution 'SHELXS-86 (Sheldrick, 1990)' _computing_structure_refinement 'SHELXL-93 (Sheldrick, 1993)' _computing_molecular_graphics 'Diamond' _computing_publication_material ? _refine_special_details ; Refinement on F^2^ for ALL reflections except for 0 with very negative F^2^ or flagged by the user for potential systematic errors. Weighted R-factors wR and all goodnesses of fit S are based on F^2^, conventional R-factors R are based on F, with F set to zero for negative F^2^. The observed criterion of F^2^ > 2sigma(F^2^) is used only for calculating _R_factor_obs etc. and is not relevant to the choice of reflections for refinement. R-factors based on F^2^ are statistically about twice as large as those based on F, and R- factors based on ALL data will be even larger. ; _refine_ls_structure_factor_coef Fsqd _refine_ls_matrix_type full _refine_ls_weighting_scheme 'calc w=1/[\s^2^(Fo^2^)+(0.0682P)^2^+35.5439P] where P=(Fo^2^+2Fc^2^)/3' _atom_sites_solution_primary direct _atom_sites_solution_secondary difmap _atom_sites_solution_hydrogens ? _refine_ls_hydrogen_treatment ? _refine_ls_extinction_method SHELXL _refine_ls_extinction_coef 0.0025(24) _refine_ls_extinction_expression 'Fc^*^=kFc[1+0.001xFc^2^\l^3^/sin(2\q)]^-1/4^' _refine_ls_number_reflns 532 _refine_ls_number_parameters 52 _refine_ls_number_restraints 0 _refine_ls_R_factor_all 0.1578 _refine_ls_R_factor_obs 0.1190 _refine_ls_wR_factor_all 0.2537 _refine_ls_wR_factor_obs 0.2374 _refine_ls_goodness_of_fit_all 1.352 _refine_ls_goodness_of_fit_obs 1.426 _refine_ls_restrained_S_all 1.352 _refine_ls_restrained_S_obs 1.426 _refine_ls_shift/esd_max 0.000 _refine_ls_shift/esd_mean 0.000 loop_ _atom_site_label _atom_site_type_symbol _atom_site_fract_x _atom_site_fract_y _atom_site_fract_z _atom_site_U_iso_or_equiv _atom_site_thermal_displace_type _atom_site_occupancy _atom_site_calc_flag _atom_site_refinement_flags _atom_site_disorder_group Si1 Si 0.5000 -0.2500 -0.1250 0.0070(13) Uani 1 d S . O1 O 0.5000 -0.0703(9) -0.0926(2) 0.012(2) Uani 1 d S . O2 O 0.5000 0.0000 0.0000 0.026(3) Uani 1 d S . Ti Ti 0.0000 0.0000 0.0000 0.0180(14) Uani 0.50 d SP . Si2 Si 0.6108(5) 0.0437(5) -0.05272(13) 0.0085(10) Uani 0.50 d P . O3 O 0.1797(13) -0.0015(14) -0.0537(4) 0.018(2) Uani 0.50 d P . O4 O 0.0000 -0.2500 -0.0012(9) 0.026(5) Uani 0.50 d SP . O5 O 0.5695(20) 0.2500 -0.0680(5) 0.019(4) Uani 0.50 d SP . Na1 Na 0.0000 -0.2500 -0.0923(6) 0.048(3) Uani 0.536(14) d SP . Na2 Na 0.0000 0.2500 -0.0946(7) 0.048(3) Uani 0.464(14) d SP . loop_ _atom_site_aniso_label _atom_site_aniso_U_11 _atom_site_aniso_U_22 _atom_site_aniso_U_33 _atom_site_aniso_U_23 _atom_site_aniso_U_13 _atom_site_aniso_U_12 Si1 0.006(2) 0.006(2) 0.009(3) 0.000 0.000 0.000 O1 0.011(3) 0.008(3) 0.017(4) -0.004(3) 0.000 0.000 O2 0.042(7) 0.017(6) 0.019(6) -0.001(5) 0.000 0.000 Ti 0.008(3) 0.032(4) 0.014(3) 0.000(2) 0.000 0.000 Si2 0.008(2) 0.005(2) 0.012(2) -0.0013(14) -0.0021(14) -0.0011(14) O3 0.012(5) 0.018(6) 0.024(5) -0.002(4) 0.007(4) -0.001(4) O4 0.046(15) 0.003(10) 0.028(12) 0.000 0.000 0.000 O5 0.034(9) 0.001(6) 0.021(7) 0.000 -0.006(6) 0.000 Na1 0.039(7) 0.060(8) 0.045(6) 0.000 0.000 0.000 Na2 0.039(7) 0.060(8) 0.045(6) 0.000 0.000 0.000 _geom_special_details ; All esds (except the esd in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell esds are taken into account individually in the estimation of esds in distances, angles and torsion angles; correlations between esds in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell esds is used for estimating esds involving l.s. planes. ; loop_ _geom_bond_atom_site_label_1 _geom_bond_atom_site_label_2 _geom_bond_distance _geom_bond_site_symmetry_2 _geom_bond_publ_flag Si1 O1 1.612(7) 28_545 ? Si1 O1 1.612(7) . ? Si1 O1 1.612(7) 10_544 ? Si1 O1 1.612(7) 19_665 ? O1 Si2 1.615(7) . ? O1 Si2 1.615(7) 22_655 ? O1 Na1 2.991(12) 19_665 ? O2 Si2 1.698(4) 6 ? O2 Si2 1.698(4) 17_655 ? O2 Si2 1.698(4) . ? O2 Si2 1.698(4) 22_655 ? Ti O4 1.8719(5) 17 ? Ti O4 1.8719(4) . ? Ti O3 1.993(10) 22 ? Ti O3 1.993(10) 6 ? Ti O3 1.993(10) . ? Ti O3 1.993(10) 17 ? Ti Na1 3.146(13) 17 ? Ti Na1 3.146(13) . ? Ti Na2 3.197(15) . ? Ti Na2 3.197(15) 17 ? Si2 O3 1.605(10) 22_655 ? Si2 O5 1.629(6) . ? Si2 Si2 1.659(7) 22_655 ? Si2 O5 2.093(11) 10_554 ? Si2 Na1 3.370(14) 19_665 ? Si2 Na2 3.492(7) 1_655 ? O3 Si2 1.605(10) 22_655 ? O3 Na1 2.528(12) . ? O3 Na2 2.571(13) . ? O4 Ti 1.8719(4) 10_444 ? O4 Na1 2.50(3) . ? O4 Na2 2.62(3) 17 ? O5 O5 1.04(3) 10_554 ? O5 Si2 1.629(6) 29 ? O5 Si2 2.093(11) 22_655 ? O5 Si2 2.093(11) 10_554 ? O5 Na1 2.51(2) 19_665 ? Na1 O5 2.51(2) 19_565 ? Na1 O5 2.51(2) 28_545 ? Na1 O3 2.528(12) 10_444 ? Na1 O3 2.528(12) 22 ? Na1 O3 2.528(12) 29_545 ? Na1 O1 2.991(12) 19_565 ? Na1 O1 2.991(12) 28_545 ? Na1 Ti 3.146(13) 10_444 ? Na1 Si2 3.370(14) 19_565 ? Na2 Na2 1.67(4) 19_565 ? Na2 O3 2.571(13) 29 ? Na2 O3 2.571(13) 22 ? Na2 O3 2.571(13) 10_454 ? Na2 O4 2.62(3) 17 ? Na2 Ti 3.197(15) 10_454 ? Na2 Si2 3.492(7) 10_554 ? Na2 Si2 3.492(7) 1_455 ? Na2 Si2 3.492(7) 22_655 ? Na2 Si2 3.492(7) 29_455 ? loop_ _geom_angle_atom_site_label_1 _geom_angle_atom_site_label_2 _geom_angle_atom_site_label_3 _geom_angle _geom_angle_site_symmetry_1 _geom_angle_site_symmetry_3 _geom_angle_publ_flag O1 Si1 O1 107.7(2) 28_545 . ? O1 Si1 O1 107.7(2) 28_545 10_544 ? O1 Si1 O1 113.1(5) . 10_544 ? O1 Si1 O1 113.1(5) 28_545 19_665 ? O1 Si1 O1 107.7(2) . 19_665 ? O1 Si1 O1 107.7(2) 10_544 19_665 ? Si1 O1 Si2 144.5(3) . . ? Si1 O1 Si2 144.5(3) . 22_655 ? Si2 O1 Si2 61.8(4) . 22_655 ? Si1 O1 Na1 109.8(4) . 19_665 ? Si2 O1 Na1 88.8(4) . 19_665 ? Si2 O1 Na1 88.8(4) 22_655 19_665 ? Si2 O2 Si2 58.5(2) 6 17_655 ? Si2 O2 Si2 121.5(2) 6 . ? Si2 O2 Si2 180.0 17_655 . ? Si2 O2 Si2 180.0 6 22_655 ? Si2 O2 Si2 121.5(2) 17_655 22_655 ? Si2 O2 Si2 58.5(2) . 22_655 ? O4 Ti O4 180.0 17 . ? O4 Ti O3 91.0(6) 17 22 ? O4 Ti O3 89.0(6) . 22 ? O4 Ti O3 89.0(6) 17 6 ? O4 Ti O3 91.0(6) . 6 ? O3 Ti O3 180.0 22 6 ? O4 Ti O3 91.0(6) 17 . ? O4 Ti O3 89.0(6) . . ? O3 Ti O3 84.9(6) 22 . ? O3 Ti O3 95.1(6) 6 . ? O4 Ti O3 89.0(6) 17 17 ? O4 Ti O3 91.0(6) . 17 ? O3 Ti O3 95.1(6) 22 17 ? O3 Ti O3 84.9(6) 6 17 ? O3 Ti O3 180.0 . 17 ? O4 Ti Na1 52.5(7) 17 17 ? O4 Ti Na1 127.5(7) . 17 ? O3 Ti Na1 126.6(3) 22 17 ? O3 Ti Na1 53.4(3) 6 17 ? O3 Ti Na1 126.6(3) . 17 ? O3 Ti Na1 53.4(3) 17 17 ? O4 Ti Na1 127.5(7) 17 . ? O4 Ti Na1 52.5(7) . . ? O3 Ti Na1 53.4(3) 22 . ? O3 Ti Na1 126.6(3) 6 . ? O3 Ti Na1 53.4(3) . . ? O3 Ti Na1 126.6(3) 17 . ? Na1 Ti Na1 180.0 17 . ? O4 Ti Na2 55.1(8) 17 . ? O4 Ti Na2 124.9(8) . . ? O3 Ti Na2 53.5(3) 22 . ? O3 Ti Na2 126.5(3) 6 . ? O3 Ti Na2 53.5(3) . . ? O3 Ti Na2 126.5(3) 17 . ? Na1 Ti Na2 107.7(3) 17 . ? Na1 Ti Na2 72.3(3) . . ? O4 Ti Na2 124.9(8) 17 17 ? O4 Ti Na2 55.1(8) . 17 ? O3 Ti Na2 126.5(3) 22 17 ? O3 Ti Na2 53.5(3) 6 17 ? O3 Ti Na2 126.5(3) . 17 ? O3 Ti Na2 53.5(3) 17 17 ? Na1 Ti Na2 72.3(3) 17 17 ? Na1 Ti Na2 107.7(3) . 17 ? Na2 Ti Na2 180.0 . 17 ? O3 Si2 O1 112.3(5) 22_655 . ? O3 Si2 O5 112.4(6) 22_655 . ? O1 Si2 O5 103.3(5) . . ? O3 Si2 Si2 167.8(4) 22_655 22_655 ? O1 Si2 Si2 59.1(2) . 22_655 ? O5 Si2 Si2 79.1(5) . 22_655 ? O3 Si2 O2 116.8(5) 22_655 . ? O1 Si2 O2 102.9(3) . . ? O5 Si2 O2 108.0(6) . . ? Si2 Si2 O2 60.76(12) 22_655 . ? O3 Si2 O5 141.5(6) 22_655 10_554 ? O1 Si2 O5 85.6(4) . 10_554 ? O5 Si2 O5 29.2(8) . 10_554 ? Si2 Si2 O5 49.9(3) 22_655 10_554 ? O2 Si2 O5 89.8(4) . 10_554 ? O3 Si2 Na1 108.9(4) 22_655 19_665 ? O1 Si2 Na1 62.5(3) . 19_665 ? O5 Si2 Na1 45.6(5) . 19_665 ? Si2 Si2 Na1 75.75(8) 22_655 19_665 ? O2 Si2 Na1 134.0(2) . 19_665 ? O5 Si2 Na1 48.1(4) 10_554 19_665 ? O3 Si2 Na2 43.3(4) 22_655 1_655 ? O1 Si2 Na2 116.1(4) . 1_655 ? O5 Si2 Na2 69.8(5) . 1_655 ? Si2 Si2 Na2 146.6(2) 22_655 1_655 ? O2 Si2 Na2 140.6(3) . 1_655 ? O5 Si2 Na2 98.4(4) 10_554 1_655 ? Na1 Si2 Na2 73.9(3) 19_665 1_655 ? Si2 O3 Ti 130.3(6) 22_655 . ? Si2 O3 Na1 133.0(6) 22_655 . ? Ti O3 Na1 87.4(4) . . ? Si2 O3 Na2 111.3(5) 22_655 . ? Ti O3 Na2 88.0(5) . . ? Na1 O3 Na2 94.5(4) . . ? Ti O4 Ti 178.0(14) 10_444 . ? Ti O4 Na1 91.0(7) 10_444 . ? Ti O4 Na1 91.0(7) . . ? Ti O4 Na2 89.0(7) 10_444 17 ? Ti O4 Na2 89.0(7) . 17 ? Na1 O4 Na2 180.0 . 17 ? O5 O5 Si2 100.9(5) 10_554 29 ? O5 O5 Si2 100.9(5) 10_554 . ? Si2 O5 Si2 142.8(9) 29 . ? O5 O5 Si2 49.9(3) 10_554 22_655 ? Si2 O5 Si2 140.4(9) 29 22_655 ? Si2 O5 Si2 51.1(3) . 22_655 ? O5 O5 Si2 49.9(3) 10_554 10_554 ? Si2 O5 Si2 51.1(3) 29 10_554 ? Si2 O5 Si2 140.4(9) . 10_554 ? Si2 O5 Si2 95.1(7) 22_655 10_554 ? O5 O5 Na1 78.1(4) 10_554 19_665 ? Si2 O5 Na1 106.9(5) 29 19_665 ? Si2 O5 Na1 106.9(5) . 19_665 ? Si2 O5 Na1 93.6(4) 22_655 19_665 ? Si2 O5 Na1 93.6(4) 10_554 19_665 ? O4 Na1 O5 168.1(4) . 19_565 ? O4 Na1 O5 168.1(4) . 28_545 ? O5 Na1 O5 23.9(7) 19_565 28_545 ? O4 Na1 O3 65.3(4) . . ? O5 Na1 O3 124.2(5) 19_565 . ? O5 Na1 O3 104.9(4) 28_545 . ? O4 Na1 O3 65.3(4) . 10_444 ? O5 Na1 O3 104.9(4) 19_565 10_444 ? O5 Na1 O3 124.2(5) 28_545 10_444 ? O3 Na1 O3 130.5(8) . 10_444 ? O4 Na1 O3 65.3(4) . 22 ? O5 Na1 O3 124.2(5) 19_565 22 ? O5 Na1 O3 104.9(4) 28_545 22 ? O3 Na1 O3 64.3(5) . 22 ? O3 Na1 O3 94.8(6) 10_444 22 ? O4 Na1 O3 65.3(4) . 29_545 ? O5 Na1 O3 104.9(4) 19_565 29_545 ? O5 Na1 O3 124.2(5) 28_545 29_545 ? O3 Na1 O3 94.8(6) . 29_545 ? O3 Na1 O3 64.3(5) 10_444 29_545 ? O3 Na1 O3 130.5(8) 22 29_545 ? O4 Na1 O1 126.7(3) . 19_565 ? O5 Na1 O1 54.2(3) 19_565 19_565 ? O5 Na1 O1 54.2(3) 28_545 19_565 ? O3 Na1 O1 132.6(3) . 19_565 ? O3 Na1 O1 79.8(2) 10_444 19_565 ? O3 Na1 O1 79.8(2) 22 19_565 ? O3 Na1 O1 132.6(3) 29_545 19_565 ? O4 Na1 O1 126.7(3) . 28_545 ? O5 Na1 O1 54.2(3) 19_565 28_545 ? O5 Na1 O1 54.2(3) 28_545 28_545 ? O3 Na1 O1 79.8(2) . 28_545 ? O3 Na1 O1 132.6(3) 10_444 28_545 ? O3 Na1 O1 132.6(3) 22 28_545 ? O3 Na1 O1 79.8(2) 29_545 28_545 ? O1 Na1 O1 106.6(5) 19_565 28_545 ? O4 Na1 Ti 36.5(2) . . ? O5 Na1 Ti 155.4(4) 19_565 . ? O5 Na1 Ti 131.6(4) 28_545 . ? O3 Na1 Ti 39.3(3) . . ? O3 Na1 Ti 95.8(5) 10_444 . ? O3 Na1 Ti 39.3(3) 22 . ? O3 Na1 Ti 95.8(5) 29_545 . ? O1 Na1 Ti 118.70(14) 19_565 . ? O1 Na1 Ti 118.70(14) 28_545 . ? O4 Na1 Ti 36.5(2) . 10_444 ? O5 Na1 Ti 131.6(4) 19_565 10_444 ? O5 Na1 Ti 155.4(4) 28_545 10_444 ? O3 Na1 Ti 95.8(5) . 10_444 ? O3 Na1 Ti 39.3(3) 10_444 10_444 ? O3 Na1 Ti 95.8(5) 22 10_444 ? O3 Na1 Ti 39.3(3) 29_545 10_444 ? O1 Na1 Ti 118.70(14) 19_565 10_444 ? O1 Na1 Ti 118.70(14) 28_545 10_444 ? Ti Na1 Ti 73.0(3) . 10_444 ? O4 Na1 Si2 148.7(2) . 19_565 ? O5 Na1 Si2 27.56(14) 19_565 19_565 ? O5 Na1 Si2 38.3(3) 28_545 19_565 ? O3 Na1 Si2 141.5(5) . 19_565 ? O3 Na1 Si2 86.1(3) 10_444 19_565 ? O3 Na1 Si2 107.1(3) 22 19_565 ? O3 Na1 Si2 114.8(4) 29_545 19_565 ? O1 Na1 Si2 28.6(2) 19_565 19_565 ? O1 Na1 Si2 81.8(4) 28_545 19_565 ? Ti Na1 Si2 146.40(8) . 19_565 ? Ti Na1 Si2 122.69(7) 10_444 19_565 ? Na2 Na2 O3 115.9(4) 19_565 29 ? Na2 Na2 O3 115.9(4) 19_565 . ? O3 Na2 O3 94.2(6) 29 . ? Na2 Na2 O3 115.9(4) 19_565 22 ? O3 Na2 O3 128.3(8) 29 22 ? O3 Na2 O3 63.1(5) . 22 ? Na2 Na2 O3 115.9(4) 19_565 10_454 ? O3 Na2 O3 63.1(5) 29 10_454 ? O3 Na2 O3 128.3(8) . 10_454 ? O3 Na2 O3 94.2(6) 22 10_454 ? Na2 Na2 O4 180.0 19_565 17 ? O3 Na2 O4 64.1(4) 29 17 ? O3 Na2 O4 64.1(4) . 17 ? O3 Na2 O4 64.1(4) 22 17 ? O3 Na2 O4 64.1(4) 10_454 17 ? Na2 Na2 Ti 144.2(2) 19_565 10_454 ? O3 Na2 Ti 38.5(3) 29 10_454 ? O3 Na2 Ti 94.3(5) . 10_454 ? O3 Na2 Ti 94.3(5) 22 10_454 ? O3 Na2 Ti 38.5(3) 10_454 10_454 ? O4 Na2 Ti 35.8(2) 17 10_454 ? Na2 Na2 Ti 144.2(2) 19_565 . ? O3 Na2 Ti 94.3(5) 29 . ? O3 Na2 Ti 38.5(3) . . ? O3 Na2 Ti 38.5(3) 22 . ? O3 Na2 Ti 94.3(5) 10_454 . ? O4 Na2 Ti 35.8(2) 17 . ? Ti Na2 Ti 71.7(4) 10_454 . ? Na2 Na2 Si2 109.2(3) 19_565 10_554 ? O3 Na2 Si2 25.4(2) 29 10_554 ? O3 Na2 Si2 75.2(3) . 10_554 ? O3 Na2 Si2 128.1(6) 22 10_554 ? O3 Na2 Si2 88.2(3) 10_454 10_554 ? O4 Na2 Si2 70.8(3) 17 10_554 ? Ti Na2 Si2 58.3(2) 10_454 10_554 ? Ti Na2 Si2 89.6(4) . 10_554 ? Na2 Na2 Si2 109.2(3) 19_565 1_455 ? O3 Na2 Si2 128.1(6) 29 1_455 ? O3 Na2 Si2 88.2(3) . 1_455 ? O3 Na2 Si2 25.4(2) 22 1_455 ? O3 Na2 Si2 75.2(3) 10_454 1_455 ? O4 Na2 Si2 70.8(3) 17 1_455 ? Ti Na2 Si2 89.6(4) 10_454 1_455 ? Ti Na2 Si2 58.3(2) . 1_455 ? Si2 Na2 Si2 141.6(6) 10_554 1_455 ? Na2 Na2 Si2 109.2(3) 19_565 22_655 ? O3 Na2 Si2 75.2(3) 29 22_655 ? O3 Na2 Si2 25.4(2) . 22_655 ? O3 Na2 Si2 88.2(3) 22 22_655 ? O3 Na2 Si2 128.1(6) 10_454 22_655 ? O4 Na2 Si2 70.8(3) 17 22_655 ? Ti Na2 Si2 89.6(4) 10_454 22_655 ? Ti Na2 Si2 58.3(2) . 22_655 ? Si2 Na2 Si2 52.5(2) 10_554 22_655 ? Si2 Na2 Si2 113.1(3) 1_455 22_655 ? Na2 Na2 Si2 109.2(3) 19_565 29_455 ? O3 Na2 Si2 88.2(3) 29 29_455 ? O3 Na2 Si2 128.1(6) . 29_455 ? O3 Na2 Si2 75.2(3) 22 29_455 ? O3 Na2 Si2 25.4(2) 10_454 29_455 ? O4 Na2 Si2 70.8(3) 17 29_455 ? Ti Na2 Si2 58.3(2) 10_454 29_455 ? Ti Na2 Si2 89.6(4) . 29_455 ? Si2 Na2 Si2 113.1(3) 10_554 29_455 ? Si2 Na2 Si2 52.5(2) 1_455 29_455 ? Si2 Na2 Si2 141.6(6) 22_655 29_455 ? _refine_diff_density_max 0.955 _refine_diff_density_min -0.691 _refine_diff_density_rms 0.174