File Name : tabela.tif

Caption : table s1. rietveld and williansom-hall results. phase fraction, lattice parameters (a, b, c), cell 
volume, average crystallite size, ρ is the williamson and smallman’s dislocation density, 
microstrain and x² is the final convergence criteria for the rietveld method. 

File Name : s1.tif

Caption : fig. s1: process for the preparation of mgo:zno. 

File Name : s2.tif

Caption : fig. s2: sem images of typical zno and mgo particles (spherical- and flake-shaped, 
respectively). 

File Name : s3.tif

Caption : figure s3: histogram results. histograms were obtained by measuring all tem images for the 
samples on imagej software. the average tem size was obtained by simple statistics and 
maximum and minimum values. 

File Name : s3_.tif

Caption : figure s3: histogram results. histograms were obtained by measuring all tem images for the 
samples on imagej software. the average tem size was obtained by simple statistics and 
maximum and minimum values. 

File Name : s3__.tif

Caption : figure s3: histogram results. histograms were obtained by measuring all tem images for the 
samples on imagej software. the average tem size was obtained by simple statistics and 
maximum and minimum values

File Name : s3___.tif

Caption : figure s3: histogram results. histograms were obtained by measuring all tem images for the 
samples on imagej software. the average tem size was obtained by simple statistics and 
maximum and minimum values. 

File Name : s4a.tif

Caption : fig. s4: tem images and eds showing the morphology and composition for mgo:zno 1:3 ((a), (b) and (c). 

File Name : s4b.tif

Caption : fig. s4: tem images and eds showing the morphology and composition for mgo:zno 1:3 ((a), (b) and (c). 

File Name : s4c.tif

Caption : fig. s4: tem images and eds showing the morphology and composition for mgo:zno 1:3 ((a), (b) and (c). 

File Name : s5.tif

Caption : fig. s5: tem images and eds showing the morphology and composition for mgo:zno 1:10. 

File Name : s6a.tif

Caption : fig. s6: tem images and eds showing the morphology and composition for mgo:zno 1:15 ((a), (b) and (c)). 

File Name : s6b.tif

Caption : fig. s6: tem images and eds showing the morphology and composition for mgo:zno 1:15 ((a), (b) and (c)). 

File Name : s6c.tif

Caption : fig. s6: tem images and eds showing the morphology and composition for mgo:zno 1:15 ((a), (b) and (c)). 

File Name : s7.tif

Caption : fig. s7: tem images and eds showing the morphology and composition for mgo:zno 1:20. 

File Name : s8.tif

Caption : fig. s8: tem images showing the morphology for mgo:zno: (a) 1:1 and insert of electron diffraction of both zno and mgo crystalline phases, showing particle crystalllinity, (b) 3:1, (c) 5:1 and (d) 10:1.  

File Name : s9.tif

Caption : fig. s9: tem images showing the morphology for mgo:zno: (a) 1:1, (b) 1:3, (c) 1:5 and (d) 1:10. 

File Name : s10.tif

Caption : fig. s10: tem images showing the morphology for mgo:zno: 1:15 ((a) and (b)), 1:20 ((c) and (d)).